PACKAGING:
Standard Rolls - Marine
Grade
|
Fabric
|
Width
|
Length
(ft)
|
Length
(m)
|
Area
(ft²)
|
Weight
(lb)
|
Weight
(kg)
|
Edges*
|
|
1.0 oz
|
38”
|
315
|
96
|
997.5
|
61.7
|
28
|
T
|
|
1.0 oz
|
50”
|
315
|
96
|
1312.5
|
81.6
|
37
|
T, 1FE
|
|
1.5 oz
|
38”
|
210
|
64
|
665
|
61.7
|
28
|
T
|
|
1.5oz
|
50”
|
210
|
64
|
875
|
81.6
|
37
|
T, 1FE
|
|
1.5 oz
|
82”
|
210
|
64
|
1435
|
132.3
|
60
|
2 FE
|
|
2.0 oz
|
41”
|
157
|
48
|
536.5
|
66.1
|
30
|
T
|
|
2.0 oz
|
49”
|
157
|
48
|
641
|
79.4
|
36
|
T
|
Standard Rolls -
Manufacturing Grade
|
Fabric
|
Width
|
Length
(ft)
|
Length
(m)
|
Area
(ft²)
|
Weight
(lb)
|
Weight
(kg)
|
Edges*
|
|
.75 oz
|
38”
|
400
|
133
|
1266.7
|
60
|
27
|
T
|
|
.75 oz
|
50”
|
405
|
135
|
1687.5
|
80
|
36
|
T
|
|
1.0 oz
|
50”
|
308.5
|
94
|
1285.5
|
80
|
36
|
2 FE
|
|
1.5 oz
|
50”
|
206.5
|
63
|
860.5
|
80
|
36
|
T, 2 FE
|
|
3 oz
|
50”
|
147.5
|
45
|
614.5
|
115
|
52
|
T
|
*
Edges
T
= Trimmed Edges
1FE
= 1 Feathered Edge
2FE
= 2 Feathered Edges
CUSTOM:
Other weights, widths or
stamping can also be supplied
SPECIAL REMARKS:
Refer to MSDS sheet
prior to use and handling.
MAT
Advanced
Chopped Strand Mat
DESCRIPTION:
Advanced
chopped strand mat is a random oriented chopped strand product composed of high quality E-glass fiber strands. These
strands are made up of many
filaments, which are protected with a silane coupling agent. The strands are cut into 5 cm
lengths and are randomly and evenly formed into a mat. The chopped strands
are bonded together with a small amount of a highly soluble polyester powder.
FEATURES:
- High degree of
uniformity
- High
translucency
- Good covering
and degassing properties
- Good mold
adaptability
- DNV, Lloyds
approvals*
*
available on marine grade product
TECHNICAL
INFORMATION:
Based on 450 g / m² (± 1½
oz/ft²) Chopped Strand Mat
Formulation: E-glass
(over 50% silica oxide - also contains oxides of
aluminum, boron, calcium
and others)
|
Property
|
Typical Value
|
|
Moisture Content
|
< 0.1 %
|
|
Binder Content
|
<3.5%
|
|
Type of Bonding
|
Polyester Powder
|
|
Sizing
|
Silane
|
|
Alkali Content
|
<0.8%
|
|
Wet Out
|
Fast
|
|
Dissolving Time in
Styrene
|
<60 seconds
|
|
Tensile Strength
(kg/20cm x 20cm) Warp
|
>90 N
|
|
Tensile Strength
(kg/20cm x 20cm) Weft
|
>80 N
|
|
Flexural Strength of
Laminate
|
>150 Mpa
|
|
Filament Diameter
|
11 pm
|
TMR 900
Advanced
TMR 900 Isophthalic Gel
Coat
DESCRIPTION:
TMR900 is a high quality Isophthalic Gel
Coat. It is available promoted or un-promoted, with or without
waxed, and with or without pigment.
TMR900
is used for various coloured FRP products (marine, cooling tower, automobile parts, etc.)
CHARACTERISTICS:
Good Weather Resistance
Good
heat resistance
Good
water resistance
Good
pigment dispersion
Good
workability
High
gloss finish
TYPICAL
PROPERTIES:
Uncured Resin*
|
Test
|
Value
|
|
Viscosity, 25◦C
|
1500-3000 cps
|
|
Thixotropic Index, 25◦
|
4.0-5.5
|
|
Gel Time, 25◦C
|
8-15 minutes
|
Cured Resin**
|
Test
|
Value
|
|
Tensile Strength
|
8.5 kg/mm²
|
|
Tensile Modulus
|
347 kg/mm²
|
|
Elongation
|
1.33%
|
|
Flexural Strength
|
12.9 kg/mm²
|
|
Flexural Modulus
|
384 kg/mm²
|
|
Barcol Hardness, 934-1
|
47
|
|
Heat Distortion Temp
|
110◦C
|
|
Resistance of Water
(25◦C x 4hr)
|
0.12%
|
|
Resistance of Boiling
Water (100◦C x 2hr)
|
0.41%
|
**
All values are typical, cured resin
Thickness: 3.0MM
Catalyst: 50% MEKP 1%
After
Cure: 25◦C x 16hrs + 80◦C x
4hrs